Low-temperature synthesis of 2D anisotropic MoTe2 using a high-pressure soft sputtering technique

Abstract

We demonstrate a high-pressure soft sputtering technique that can grow large area 1T′ phase MoTe2 sheets on HOPG and Al2O3 substrates at temperatures as low as 300 °C. The results show that a single Mo/Te co-sputtering step on heated substrates produces highly defected films as a result of the low Te sticking coefficient. The stoichiometry is significantly improved when a 2-step technique is used, which first co-sputters Mo and Te onto an unheated substrate and then anneals the deposited material to crystalize it into 1T′ phase MoTe2. A MoTe2−x 1T′ film with the lowest Te vacancy content (x = 0.14) was synthesized using a 300 °C annealing step, but a higher processing temperature was prohibited due to MoTe2 decomposition with an activation energy of 80.7 kJ mol−1. However, additional ex situ thermal processing at ∼1 torr tellurium pressure can further reduce the Te-vacancy (VTe) concentration, resulting in an improvement in the composition from MoTe1.86 to MoTe1.9. Hall measurements indicate that the films produced with the 2-step in situ process are n-type with a carrier concentration of 4.6 × 1014 cm−2 per layer, presumably from the large VTe concentration stabilizing the 1T′ over the 2H phase. Our findings (a) demonstrate that large scale synthesis of tellurium based vdW materials is possible using industrial growth and processing techniques and (b) accentuate the challenges in producing stoichiometric MoTe2 thin films.

Graphical abstract: Low-temperature synthesis of 2D anisotropic MoTe2 using a high-pressure soft sputtering technique

Supplementary files

Article information

Article type
Paper
Submitted
09 Dec 2019
Accepted
13 Feb 2020
First published
04 Mar 2020
This article is Open Access
Creative Commons BY license

Nanoscale Adv., 2020,2, 1443-1448

Low-temperature synthesis of 2D anisotropic MoTe2 using a high-pressure soft sputtering technique

K. Yumigeta, C. Kopas, M. Blei, D. Hajra, Y. Shen, D. Trivedi, P. Kolari, N. Newman and S. Tongay, Nanoscale Adv., 2020, 2, 1443 DOI: 10.1039/D0NA00066C

This article is licensed under a Creative Commons Attribution 3.0 Unported Licence. You can use material from this article in other publications without requesting further permissions from the RSC, provided that the correct acknowledgement is given.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements