Highly efficient dye-sensitized solar cell with a ZnO nanosheet-based photoanode

Abstract

Zinc oxide (ZnO) nanosheets (ZnO-NS) were prepared for the photoanode of a dye-sensitized solar cell (DSSC), first by directly growing layered hydroxide zinc carbonate (LHZC) on an FTO substrate using a chemical bath deposition (CBD) method and then by transforming the LHZC into ZnO through pyrolysis at 300 °C. A light-to-electricity conversion efficiency (η) of 6.06% was achieved for the DSSC with ZnO-NS as its photoanode, under 100 mW cm−2 illumination, and this (η) was found to be much higher than that of the DSSC with ZnO nanoparticles (ZnO-NP) as the photoanode (2.92%). The far superior performance of the DSSC with ZnO-NS is essentially attributed to (i) higher effective electron diffusion coefficient of ZnO-NS (3.59 × 10−3 cm2s−1) than that of ZnO-NP (1.12 × 10−3 cm2s−1), and to (ii) higher dye loading on ZnO-NS (2.66 × 10−7 mol cm−2) than that on ZnO-NP (1.99 × 10−7 mol cm−2); this higher electron diffusion coefficient and dye-loading are attributed to the specific morphology of the ZnO-NS. A further improvement in the efficiency of the DSSC with ZnO-NS could be achieved through the electrophoretic deposition (EPD) of a very thin layer (3 μm) of titanium dioxide nanoparticles (TiO2-NPs of average size 14 nm) onto the ZnO-NS layer (12 μm). Notwithstanding a decrease in the effective electron diffusion coefficient (3.07 × 10−3 cm2s−1) in the TiO2-NP/ZnO-NS film, with reference to that in the ZnO-NS film (3.59 × 10−3 cm2s−1), a far higher cell efficiency was obtained in favor of the cell with TiO2-NP/ZnO-NS (7.07%), compared to that of the cell with bare ZnO-NS (6.06%); this enhancement in the η of the cell with TiO2-NP/ZnO-NS is ascribed to an increased dye-loading in favor of its cell (3.92 × 10−7 mol cm−2), with reference to that in the case of the cell with bare ZnO-NS (2.66 × 10−7 mol cm−2). As against the common ruthenium dyes, such as N3 and N-719, a metal-free dye, coded as D149, was used in this research. The efficiency achieved for the best DSSC in this work is the highest ever reported for a DSSC with ZnO as the main semiconductor material.

Graphical abstract: Highly efficient dye-sensitized solar cell with a ZnO nanosheet-based photoanode

Supplementary files

Article information

Article type
Paper
Submitted
24 Oct 2010
Accepted
20 May 2011
First published
06 Jul 2011

Energy Environ. Sci., 2011,4, 3448-3455

Highly efficient dye-sensitized solar cell with a ZnO nanosheet-based photoanode

C. Lin, Y. Lai, H. Chen, J. Chen, C. Kung, R. Vittal and K. Ho, Energy Environ. Sci., 2011, 4, 3448 DOI: 10.1039/C0EE00587H

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements