High performance ordered mesoporous carbon/carbon nanotube composite electrodes for capacitive deionization

Abstract

In this study, a novel ordered mesoporous carbon/carbon nanotube (OMC/CNT) composite electrode was proposed and its capacitive deionization properties were investigated in aqueous solution. The OMC/CNT composites were obtained by an organic–inorganic self-assembly route. SEM and TEM observations show the 2D hexagonally ordered mesoporous channels and nanotubular morphology of the composites. The OMC/CNT composites with high specific surface area and excellent conductivity are favorable for capacitance deionization due to the easily available electrochemical double layer behaviors. The electrochemical properties are measured by cyclic voltammetry, galvanostatic charge/discharge, and electrochemical impedance spectroscopy measurements. Through all the measurements above, it was found that the OMC/CNT electrodes with 10 wt% of CNTs exhibit superiority in electrosorption capacitance, low resistance, high reversibility and electrochemical stability during the charge/discharge process. The comparative electrosorption properties of the OMC/CNT electrodes were also investigated in various aqueous solutions, and it is found that the electrosorption capability of the OMC/CNT electrodes depends on the hydration radius and valence of the ions in the aqueous solutions. The power and energy density were evaluated by a pair of OMC/CNT electrodes with various current loads, and this showed that the OMC/CNT composite electrodes have higher power density and lower energy density characteristics as compared with the pristine OMC electrode, which indicates that the composite electrodes exhibit low energy consumption for capacitive deionization. In desalination measurements, the OMC/CNT composite electrodes exhibit excellent desalination behavior in a flow-through apparatus, which is attributed to the low resistance and high specific surface area.

Graphical abstract: High performance ordered mesoporous carbon/carbon nanotube composite electrodes for capacitive deionization

Supplementary files

Article information

Article type
Paper
Submitted
21 Dec 2011
Accepted
08 Feb 2012
First published
24 Feb 2012

J. Mater. Chem., 2012,22, 6603-6612

High performance ordered mesoporous carbon/carbon nanotube composite electrodes for capacitive deionization

Z. Peng, D. Zhang, L. Shi and T. Yan, J. Mater. Chem., 2012, 22, 6603 DOI: 10.1039/C2JM16735B

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Spotlight

Advertisements