Abstract

Laser irradiation of colloidal mixtures consisting of Au–Pd and Ag–Pd were conducted to synthesize Au/Pd and Ag/Pd alloy nanoparticles. Compositional ratios of 1∶1 and 2∶1 were prepared in both the Au/Pd and Ag/Pd systems. The compositions, the particle sizes, and the morphology were measured as a function of the laser irradiation period in order to monitor the changes from the two-component mixtures into the alloy colloids. The average particle sizes of the 1∶1 and 2∶1 metal ratios were 3.9 ± 1.2 nm and 4.3 ± 1.1 nm, respectively, for Au/Pd and 7.3 ± 2.0 nm and 5.4 ± 2.0 nm, respectively, for Ag/Pd. However, Ag/Pd with a 2∶1 ratio had difficult in forming dispersed spherical particles and the expected compositions. In addition to EDX analysis, X-ray diffraction measurements were carried out to confirm the formation of the alloy nanoparticles.