Pore formation in silicon by wet etching using micrometre-sized metal particles as catalysts

Abstract

Au, Pt, or Ag particles with particle sizes of ca. 1 μm were used as catalysts for boring pores in p-type Si(100) wafers by wet etching in aqueous solutions containing hydrofluoric acid and hydrogen peroxide. Boring speed was fastest when Pt particles were used as the catalyst. However, the sidewalls of the pores and the surface of the wafer were covered with a nanoporous silicon layer of ca. 500 nm in thickness, and the pore showed a tapered structure. When micrometre-sized Ag particles were used, no deep pores were formed because the particles were unstable in the solution. In contrast to Pt and Ag particles, Au particles bored straight pores under some conditions. However, the morphology of pores depended on the shape of the Au particles. Spherical Au particles formed straight pores, whereas non-spherical Au particles formed pores with spiral sidewalls. When Au particles formed aggregates consisting of a small number of particles (<10 particles), crooked pores tended to be formed. In contrast, when the aggregates were composed of a larger number of particles, straight pores were formed and the boring speed was faster than the pores formed with isolated Au particles.

Graphical abstract: Pore formation in silicon by wet etching using micrometre-sized metal particles as catalysts

Article information

Article type
Paper
Submitted
10 Oct 2007
Accepted
19 Dec 2007
First published
21 Jan 2008

J. Mater. Chem., 2008,18, 1015-1020

Pore formation in silicon by wet etching using micrometre-sized metal particles as catalysts

C. Lee, K. Tsujino, Y. Kanda, S. Ikeda and M. Matsumura, J. Mater. Chem., 2008, 18, 1015 DOI: 10.1039/B715639A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Spotlight

Advertisements