Enhanced charge collection efficiency by thin-TiO2-film deposition on FTO-coated ITO conductive oxide in dye-sensitized solar cells

Abstract

We have investigated effect of thin TiO2 layers deposited on an indium tin oxide (ITO)/fluorine-doped tin oxide (FTO) double-layered transparent conductive oxide on the performance of dye-sensitized solar cell. FTO is deposited on an ITO-coated glass, followed by TiO2 deposition using a radio frequency magnetron sputtering technique. The thicknesses of the sputtered-TiO2 layers are varied from 10 nm to 20 nm, while the ITO and FTO are fixed to be 150 nm and 70 nm, respectively. Atomic force microscopy (AFM) shows that the surface roughness is similar but the surface morphology is altered by thin TiO2 layer deposition. The sheet resistance of the ITO/FTO conductive glass is hardly changed by thin TiO2 layer deposition. Photovoltaic performance is significantly enhanced after introduction of thin TiO2 underlayer. The 15 nm thick TiO2 underlayer leads to the increases of photocurrent density from 9 mA cm−2 to 10.3 mA cm−2 and fill factor from 0.715 to 0.747, as a result, the overall conversion efficiency is improved from 5.28% to 6.37%, corresponding to 20.6% increase. Photovoltage, however, remains almost unchanged. Photocurrent is improved over the entire wavelength. The increased transmittance at wavelength ranging from 300 to 600 nm contributes in part to increase in photocurrent. Improvement of charge collection efficiency from ∼90% to ∼97% is also attributed to the increased photocurrent, where the increased transport rate is responsible for the improved charge collection, indicating that the thin TiO2 underlayer has influence on opto-electronic property in the dye-adsorbed bulk TiO2 film.

Graphical abstract: Enhanced charge collection efficiency by thin-TiO2-film deposition on FTO-coated ITO conductive oxide in dye-sensitized solar cells

Article information

Article type
Paper
Submitted
14 Dec 2009
Accepted
09 Mar 2010
First published
23 Apr 2010

J. Mater. Chem., 2010,20, 4392-4398

Enhanced charge collection efficiency by thin-TiO2-film deposition on FTO-coated ITO conductive oxide in dye-sensitized solar cells

B. Yoo, K. Kim, D. Lee, M. J. Ko, H. Lee, Y. H. Kim, W. M. Kim and N. Park, J. Mater. Chem., 2010, 20, 4392 DOI: 10.1039/B926145A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Spotlight

Advertisements