Product integration of compact roll-to-roll processed polymer solar cell modules: methods and manufacture using flexographic printing, slot-die coating and rotary screen printing

Abstract

The improvement of the performance of roll-to-roll processed polymer solar cell modules through miniaturization of the device outline is described. The devices were prepared using full roll-to-roll processing comprising flexographic printing, slot-die coating and rotary screen printing to create 5 mm wide lines of ZnO, P3HT:[60/70]PCBM, PEDOT:PSS and silver on an ITO-PET substrate. The lines were spaced by 1 mm and the devices were completed by encapsulation using roll-to-roll lamination on both sides using a pressure sensitive adhesive and a multilayered barrier material having a UV-filter with a cut-off at 390 nm, oxygen and water vapor transmission rates of respectively 0.01 cm3 m−2 bar−1 day−1 and 0.04 g m−2 day−1. The final modules comprised 16 serially connected cells. The technical yield was 89% based on the criterion that the Voc had to be larger than 7.2 V. This set of modules gave respectively a voltage, current, fill factor and power conversion efficiency of 8.47 ± 0.41 V, −23.20 ± 4.10 mA, 35.4 ± 2.8% and 1.96 ± 0.34% in the case of modules based on P3HT:[60]PCBM. A total of 1960 modules were prepared for each run and the best power conversion reached was 2.75% for devices based on P3HT:[70]PCBM. The solar cell modules were used to demonstrate the complete manufacture of a small lamp entirely using techniques of flexible electronics. The solar cell module was used to charge a polymer lithium ion battery through a blocking diode. The entire process was fully automated and demonstrates the capacity of polymer solar cells in the context of flexible and printed electronics. Finally a comparison was made between the learning curve for OPV and crystalline silicon solar cells in terms of the cost per watt peak and the cumulative watt peak. OPV as a technology was found to have a significantly steeper learning curve.

Graphical abstract: Product integration of compact roll-to-roll processed polymer solar cell modules: methods and manufacture using flexographic printing, slot-die coating and rotary screen printing

Article information

Article type
Application
Submitted
23 Apr 2010
Accepted
21 May 2010
First published
08 Jul 2010

J. Mater. Chem., 2010,20, 8994-9001

Product integration of compact roll-to-roll processed polymer solar cell modules: methods and manufacture using flexographic printing, slot-die coating and rotary screen printing

F. C. Krebs, J. Fyenbo and M. Jørgensen, J. Mater. Chem., 2010, 20, 8994 DOI: 10.1039/C0JM01178A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Spotlight

Advertisements