Spacious and mechanically flexible mesoporous silica thin film composed of an open network of interlinked nanoslabs

Abstract

Transparent and smooth silica thin films with a very high porosity were prepared by linking zeolitic nanoslabs into open mesoporous networks. Calcined films characterized by ellipsometric porosimetry presented pore sizes in the range of 6–18 nm and porosities of 70–90% depending on the temperature of assembly of the nanoslabs in the presence of Pluronic P123 triblock copolymer. The films were disordered according to grazing incidence small angle X-ray scattering and transmission electron microscopy. The most spacious film had a very low refractive index of 1.08 (at 632.8 nm) and exhibited reversible shrinkage of up to 30% of its original thickness upon capillary condensation of adsorbate vapor. The mechanical flexibility of the film was confirmed by the low Young modulus of 0.9 GPa determined by nano-indentation. The full accessibility of the porosity and the convenience for chemical functionalization were demonstrated using Atomic Layer Deposition (ALD) of TiO2 monitored with Rutherford Backscattering Spectroscopy. Using ALD the porosity and mechanical flexibility of the film could be fine tuned.

Graphical abstract: Spacious and mechanically flexible mesoporous silica thin film composed of an open network of interlinked nanoslabs

Article information

Article type
Paper
Submitted
18 Jan 2011
Accepted
24 Mar 2011
First published
20 Apr 2011

J. Mater. Chem., 2011,21, 7692-7699

Spacious and mechanically flexible mesoporous silica thin film composed of an open network of interlinked nanoslabs

S. P. Sree, J. Dendooven, D. Smeets, D. Deduytsche, A. Aerts, K. Vanstreels, M. R. Baklanov, J. W. Seo, K. Temst, A. Vantomme, C. Detavernier and J. A. Martens, J. Mater. Chem., 2011, 21, 7692 DOI: 10.1039/C1JM10270B

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Spotlight

Advertisements