Electrochemical deposition and photoelectrochemistry of CuWO4, a promising photoanode for wateroxidation

Abstract

Polycrystalline thin film photoanodes composed of CuWO4 have been prepared by electrodeposition from an acidic aqueous solution. This 2–3 μm thick n-type material has an indirect band gap of 2.25 eV, 0.45 V smaller than the gap of WO3. The flat band potential and donor density determined by Mott–Schottky analysis of the electrochemical impedance spectra are +0.4 V (vs. NHE) and 2.7 × 1021 cm−3 respectively, similar to those observed in crystalline WO3. This implies that the lower band gap is due to a raised valence band maximum, desirable for water oxidation photoanodes. Under neutral conditions afforded by a pH 7 potassium phosphate buffer, electrodeposited CuWO4 generates a photocurrent density of 0.16 mA cm−2 at an applied bias of +0.5 V (vs Ag/AgCl) under simulated solar irradiation. Electrodeposited CuWO4 films demonstrate higher chemical stability than polycrystalline WO3, both under continuous illumination and in the dark. CuWO4 oxidizes methanol and maintains a stable steady-state photocurrent density of 0.11 mA cm−2 after 12 h of continuous illumination in a 10% methanol solution in aqueous electrolyte. This is twice the current density observed without methanol added.

Graphical abstract: Electrochemical deposition and photoelectrochemistry of CuWO4, a promising photoanode for water oxidation

Supplementary files

Article information

Article type
Paper
Submitted
07 Feb 2011
Accepted
29 Mar 2011
First published
18 Apr 2011

J. Mater. Chem., 2011,21, 7651-7660

Electrochemical deposition and photoelectrochemistry of CuWO4, a promising photoanode for water oxidation

J. E. Yourey and B. M. Bartlett, J. Mater. Chem., 2011, 21, 7651 DOI: 10.1039/C1JM11259G

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Spotlight

Advertisements