Gamma-radiolysis-assisted cobalt oxide nanoparticle formation

Abstract

The formation of Co3O4 nano-scale colloid particles by gamma irradiation of CoSO4 solutions was investigated. Solutions of 0.2–0.3 mM CoSO4 at pH 6.0 and 10.6 (air-saturated and Ar-purged) were irradiated at an absorbed dose rate of 5.5 kGy h−1. The resulting concentrations of H2, H2O2, CoII and CoIII species in solution and the chemical composition and sizes of particles that were formed were measured as a function of irradiation time. Particle formation was observed only for initially air-saturated CoSO4 solutions at pH 10.6. Analysis of the particle formation as a function of irradiation time shows that the particles evolve from Co(OH)2 to CoOOH and then to Co3O4. The radiolytic oxidation of CoII to CoIII was completed in 100 min and the chemical composition of the final particles was identified as Co3O4 by XPS, Raman and UV-Vis spectroscopy. Transmission electron microscopy (TEM) images show the final particles are approximately uniform in size, ranging from 8 to 20 nm. A mechanism is proposed to explain the particle formation. A key factor is the low solubility of Co(OH)2 in air-saturated solutions at high pH. This mechanism for particle formation is compared with the mechanism previously reported for the radiolytic formation of γ-FeOOH nanoparticles.

Graphical abstract: Gamma-radiolysis-assisted cobalt oxide nanoparticle formation

Article information

Article type
Paper
Submitted
04 Sep 2012
Accepted
07 Nov 2012
First published
14 Nov 2012

Phys. Chem. Chem. Phys., 2013,15, 1014-1024

Gamma-radiolysis-assisted cobalt oxide nanoparticle formation

L. M. Alrehaily, J. M. Joseph, M. C. Biesinger, D. A. Guzonas and J. C. Wren, Phys. Chem. Chem. Phys., 2013, 15, 1014 DOI: 10.1039/C2CP43094K

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements