The balance between intramolecular hydrogen bonding, polymer solubility and rigidity in single-chain polymeric nanoparticles

Abstract

A library of copolymers with pendant, protected ureido-pyrimidinone (UPy) groups was prepared applying controlled polymerization techniques. The polymer backbones were based on polyacrylate, polymethacrylate, polystyrene and polynorbornene and differ in stiffness, molecular weight and the linking moiety between the backbone and the UPy group. In all cases, the percentage of protected UPy groups was kept constant. The effect of solvent on the behaviour of the polymers before and after removal of the protecting groups was evaluated in, among others, chloroform and tetrahydrofuran (THF). After deprotection of the UPy protecting group, the UPys dimerize via four-fold H-bonding in THF, inducing a collapse into single-chain polymeric nanoparticles (SCPNs), as evidenced by a combination of 1H-NMR spectroscopy, size-exclusion chromatography and dynamic light scattering. In chloroform, on the other hand, dimerization of the UPy groups is present but interchain interactions occur as well, resulting in less-defined SCPNs. Remarkably, the flexibility of the polymer backbone, the polymer molecular weight and the nature of the linker unit all do not affect SCPN formation. In contrast, the interaction between solvent and the UPy moiety is a critical parameter for SCPN formation. For example, strong intramolecular dimerization of the UPys is observed in THF while interparticle interactions are suppressed. From this investigation we conclude that a wide variety of polymer backbones are suitable for polymer collapse via supramolecular interactions and thus allow for the formation of SCPNs but that the solvent choice is crucial to enhance intramolecular H-bonding and, at the same time, to suppress interparticle interactions.

Graphical abstract: The balance between intramolecular hydrogen bonding, polymer solubility and rigidity in single-chain polymeric nanoparticles

Supplementary files

Article information

Article type
Paper
Submitted
19 Jan 2013
Accepted
12 Feb 2013
First published
13 Feb 2013
This article is Open Access
Creative Commons BY license

Polym. Chem., 2013,4, 2584-2597

The balance between intramolecular hydrogen bonding, polymer solubility and rigidity in single-chain polymeric nanoparticles

P. J. M. Stals, M. A. J. Gillissen, R. Nicolaÿ, A. R. A. Palmans and E. W. Meijer, Polym. Chem., 2013, 4, 2584 DOI: 10.1039/C3PY00094J

This article is licensed under a Creative Commons Attribution 3.0 Unported Licence. You can use material from this article in other publications without requesting further permissions from the RSC, provided that the correct acknowledgement is given.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements