Hierarchically tetramodal-porous zeolite ZSM-5 monoliths with template-free-derived intracrystalline mesopores

Abstract

In this work, we report a unique synthesis of hierarchical zeolite ZSM-5 monoliths using polyurethane foam (PUF) as a rigid scaffold through a simple steam-assisted crystallization (SAC) method. The resultant monolithic ZSM-5 with a well crystalline structure possesses unique tetra-modal porosity (macropore/macropore/mesopore/micropore). The first modes of macroporosity (pore size of ∼33 μm) is formed after the removal of the PUF scaffolds. The second set of macropores with a size of 0.2–1.7 μm originate from the aggregation of ZSM-5 nanocrystals (crystal size of ∼500 nm) inside the macropores of the PUF scaffolds. The third level of porosity stems from the intracrystalline mesopores (∼53 nm) in each ZSM-5 crystal, along with the fourth intrinsic microporosity of zeolites. The mesopores are derived from the voids formed in the initial dry precursors, which are transformed and preserved as intracrystalline mesopores in each zeolite crystal. This type of ZSM-5 monolith possesses a high macroporosity (75.2%) and mechanical stability (1.2 MPa). The total surface area of the monolithic ZSM-5 is ∼226 m2 g−1 and the total pore volume is ∼0.21 cm3 g−1. The ZSM-5 monolith as a structured catalyst for methanol to propylene (MTP) conversion shows excellent catalytic performance with high methanol conversion (above 95%) and propylene selectivity (above 40%) at a high weight hourly space velocity (WHSV, 3.6 h−1). Importantly, the diffusion efficiency of catalyst is remarkably improved. After reaction for 5 h, the selectivity of propylene reaches a steady state.

Graphical abstract: Hierarchically tetramodal-porous zeolite ZSM-5 monoliths with template-free-derived intracrystalline mesopores

Supplementary files

Article information

Article type
Edge Article
Submitted
06 Oct 2013
Accepted
18 Dec 2013
First published
18 Dec 2013

Chem. Sci., 2014,5, 1565-1573

Hierarchically tetramodal-porous zeolite ZSM-5 monoliths with template-free-derived intracrystalline mesopores

B. Li, Z. Hu, B. Kong, J. Wang, W. Li, Z. Sun, X. Qian, Y. Yang, W. Shen, H. Xu and D. Zhao, Chem. Sci., 2014, 5, 1565 DOI: 10.1039/C3SC52779D

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements