Charge transfer and recombination at the metal oxide/CH3NH3PbClI2/spiro-OMeTAD interfaces: uncovering the detailed mechanism behind high efficiency solar cells

Abstract

In recent years, organometal halide perovskite-based solid-state hybrid solar cells have attracted unexpected increasing interest because of their high efficiency (the record power conversion efficiency has been reported to be over 15%) and low fabrication cost. It has been accepted that the high efficiency was mainly attributed to the strong optical absorption (absorption coefficient: 15 000 cm⁻¹ at 550 nm) over a broader range (up to 800 nm) and the long lifetimes of photoexcited charge carriers (in the order of 10 ns – a few 100 ns) of the perovskite absorbers. However, much of the fundamental photophysical properties of perovskite relating to the high photovoltaic performance are remained to be investigated. The charge separation and recombination processes at the material interfaces are particularly important for solar cell performances. To better understand the high efficiency of perovskite solar cells, we systematically investigated the charge separation (electron and hole injection) and charge recombination dynamics of CH₃NH₃PbClI₂ hybrid solar cells employing TiO₂ nanostructures as the electron transfer material (ETM) and spiro-OMeTAD as the hole transfer material (HTM). The measurements were carried out using transient absorption (TA) techniques on a time scale from sub-picoseconds to milliseconds. We clarified the timescales of electron injection, hole injection, and recombination processes in TiO₂/CH₃NH₃PbClI₂/spiro-OMeTAD solar cells. Charge separation and collection efficiency of the perovskite-based solar cells were discussed. In addition, the effect of TiO₂ size on the charge separation and recombination dynamics was also investigated. It was found that all TiO₂-based perovskite solar cells possessed similar charge separation processes, but quite different recombination dynamics. Our results indicate that charge recombination was crucial to the performance of the perovskite solar cells, which could be effectively suppressed through optimising nanostructured TiO₂ films and surface passivation, thus pushing these cells to even higher efficiency.