Nanostructuring of nanoporous iron carbide spheres via thermal degradation of triple-shelled Prussian blue hollow spheres for oxygen reduction reaction

Abstract

A template free strategy for designing hollow Prussian blue (PB) spheres with multi-shells is reported here. Small PB seeds were synthesized under optimized conditions using polyvinylpyrrolidone as a controlling agent. The large crystals grow from the smaller ones which have higher solubility. Voids gradually grow in the core of the large aggregates and the shell thickness increases owing to the outward diffusion of the solutes through the permeable shell leading to core–shell structure. Many shells could form at the surface of the core–shell structure through a step-by-step epitaxial crystal growth. A subsequent etching leads to the formation of triple-shelled PB hollow spheres. Likewise, a controlled thermal treatment under nitrogen yielded nanoporous iron carbide hollow spheres. The morphology is well-retained after the thermal treatment at 450 °C and completely destroyed at 700 °C because of the crystallization of the metal framework and the fusion of the pores. Nanoporous iron carbide demonstrates an efficient electrocatalytic activity for the oxygen reduction reaction. It shows a better durability than the commercial PtC-5% catalyst, with only 8% loss of the current density during the first 3500 s.

Graphical abstract: Nanostructuring of nanoporous iron carbide spheres via thermal degradation of triple-shelled Prussian blue hollow spheres for oxygen reduction reaction

Associated articles

Supplementary files

Article information

Article type
Paper
Submitted
18 Nov 2015
Accepted
18 Jan 2016
First published
21 Jan 2016

RSC Adv., 2016,6, 10341-10351

Author version available

Nanostructuring of nanoporous iron carbide spheres via thermal degradation of triple-shelled Prussian blue hollow spheres for oxygen reduction reaction

M. B. Zakaria, RSC Adv., 2016, 6, 10341 DOI: 10.1039/C5RA24357B

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements