Tuning the properties of poly(2,6-dimethyl-1,4-phenylene oxide) anion exchange membranes and their performance in H2/O2 fuel cells

Abstract

Here, we present a complete investigation of poly(2,6-dimethyl-1,4-phenylene) (PPO) AEMs with quaternary ammonium (QA) groups placed at different locations within the chemical structure of the polymer, e.g. a standard benzyltrimethyl ammonium control (BTMA), side-chain-type (SCQA), long side-chain-type (LSCQA), comb-shaped (CQA), or side-chain type/comb-shaped (SCCQA) AEMs have been designed and studied. These copolymers possess a similar composition but considerably different molecular architectures, the nature of which significantly alters their properties and device performance. Hydroxide conductivity was improved for the SCQA, LSCQA and comb-shaped membranes possessing a C-18 alkyl terminal pendant compared to that of BTMA and comb-shaped samples with a short alkyl chain. In chemical stability experiments under 10 M NaOH and 80 °C for 200 hours, LSCQA and SCCQA samples with a C-18 alkyl terminal pendant architecture showed less decrease in conductivity (∼10%) than the BTMA, SCQA and SCCQA polymers having short alkyl chains, which lost more than 50% conductivity after alkaline stability testing. Significant degradation was observed for the unstable PPO AEM samples by either SN2 substitution or Hoffmann elimination according to 1H NMR analysis. Interestingly, the fuel cell device performance provided counterintuitive data that showed that longer side chains with excellent alkaline stability were not superior in device function assessment. Specifically, the highly alkaline stable long side-chain-type LSCQA-30 membrane showed significant degradation in a fuel cell device with an operating lifetime of 3.3 h at 100 mA cm−2. Analysis of the aged membrane showed SN2 substitution and elimination of trimethylamine to be the dominant degradation mechanisms. In contrast, the BTMA-30 membranes with poor alkaline stability showed good durability in a working device without obvious degradation after 8.3 h operation as confirmed by 1H NMR spectra. This new finding that contrasts membrane alkaline stability and device operation stability is extremely important and gives us directions for new polymer designs for high performance devices. Additionally, this study paves the way for coupled ex situ chemical stability and in-device degradation studies, which are sorely needed in this field.

Graphical abstract: Tuning the properties of poly(2,6-dimethyl-1,4-phenylene oxide) anion exchange membranes and their performance in H2/O2 fuel cells

Supplementary files

Article information

Article type
Paper
Submitted
29 Aug 2017
Accepted
22 Dec 2017
First published
02 Jan 2018

Energy Environ. Sci., 2018,11, 435-446

Tuning the properties of poly(2,6-dimethyl-1,4-phenylene oxide) anion exchange membranes and their performance in H2/O2 fuel cells

L. Liu, X. Chu, J. Liao, Y. Huang, Y. Li, Z. Ge, M. A. Hickner and N. Li, Energy Environ. Sci., 2018, 11, 435 DOI: 10.1039/C7EE02468A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements