Nanoscale in situ detection of nucleation and growth of Li electrodeposition at various current densities

Abstract

Li metal batteries can store at least ten times more energy than currently existing Li-ion batteries. However, during routine charging and discharging, Li dendrites grow on the Li metal electrode, which can lead to capacity loss by the consumption of Li salt at the surface of the Li dendrites, and be a safety hazard resulting from the potential for short-circuits. Although past efforts have provided useful information about the morphology and surface area of Li dendrite formation at the microscale, a nanoscale understanding of nucleation and growth of Li nanoparticle electrodeposition is still elusive. In this study, using a new electrochemical cell for transmission mode grazing incidence small angle X-ray scattering, we obtained, for the first time, the primary nucleus size of Li nanoparticles, their size evolution and their fractal structures at various current densities and in real-time. The measured average radius of gyration, Rg, at current densities of 0.1, 0.5, and 2.0 mA cm−2 is 5.4 ± 0.4, 4.5 ± 0.3, and 3.5 ± 0.3 nm, respectively. This variation in size with current density is noteworthy when recognizing that the surface area-to-volume ratio of the Li nanoparticles is 3.7 times higher at 2.0 mA cm−2 than at 0.1 mA cm−2. We also compared a hierarchical fractal structure of Li particles from the nanometer to micrometer scale. Our findings illuminate the role of overpotential in the reactive surface area of Li dendrites at the nanoscale, and provide a novel research platform for suppressing Li dendrite formation in Li metal battery systems.

Graphical abstract: Nanoscale in situ detection of nucleation and growth of Li electrodeposition at various current densities

Supplementary files

Article information

Article type
Communication
Submitted
11 Jan 2018
Accepted
02 Feb 2018
First published
02 Feb 2018

J. Mater. Chem. A, 2018,6, 4629-4635

Nanoscale in situ detection of nucleation and growth of Li electrodeposition at various current densities

H. Jung, B. Lee, M. Lengyel, R. Axelbaum, J. Yoo, Y. S. Kim and Y. Jun, J. Mater. Chem. A, 2018, 6, 4629 DOI: 10.1039/C8TA00343B

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements