Ag nanoparticle/ZnO hollow nanosphere arrays: large scale synthesis and surface plasmon resonance effect induced Raman scattering enhancement

Abstract

ZnO hollow nanosphere (HNS) arrays decorated with Ag nanoparticles (NPs) were fabricated on silicon substrates using self-assembled monolayer polystyrene (PS) nanospheres as the template. The O2 plasma etching was introduced to manipulate the diameters of the ZnO HNSs. This fabrication method has the advantages of simplicity, large scale production, easy size and shape manipulations, low cost and bio-compatibility. Scanning electron microscopy (SEM) images show that the obtained Ag NP–ZnO HNS hybrid structures are hexagonally arranged, with the uniform size and shape, and the X-ray diffraction (XRD) pattern shows that the ZnO HNS arrays are of high crystal quality and have a dominant orientation of <0001> direction. Resonant Raman scattering spectra reveal the multiphonon A1 (LO) modes of ZnO hollow nanospheres at 574, 1147 and 1725 cm−1. Enhanced resonant Raman scattering from the Ag NP modified ZnO HNSs was observed, indicating a strong energy coupling effect located at the metal/semiconductor interface. Surface enhanced Raman scattering (SERS) application for the Ag NP decorated ZnO HNS arrays was verified using a Rhodamine 6G (R6G) chromophore as a standard analyte, which is proved to be an effective SERS template for Raman signal detection. SERS substrates with different structures have been compared, and the Ag NP modified ZnO HNS system exhibits superior Raman scattering enhancements induced by the local surface plasmon resonance (LSPR) effect. The SERS mechanism was well explained by theoretical calculation results. This study is helpful to fabricate controllable Ag NP arrays using the ZnO HNS as the supporting structure and to understand the mechanism of bio-sensing enhancements due to the LSPR effect originated from the metal NPs and metal/semiconductor interface.

Graphical abstract: Ag nanoparticle/ZnO hollow nanosphere arrays: large scale synthesis and surface plasmon resonance effect induced Raman scattering enhancement

Supplementary files

Article information

Article type
Paper
Submitted
19 Nov 2011
Accepted
22 Feb 2012
First published
12 Mar 2012

J. Mater. Chem., 2012,22, 7902-7909

Ag nanoparticle/ZnO hollow nanosphere arrays: large scale synthesis and surface plasmon resonance effect induced Raman scattering enhancement

J. Yin, Y. Zang, C. Yue, Z. Wu, S. Wu, J. Li and Z. Wu, J. Mater. Chem., 2012, 22, 7902 DOI: 10.1039/C2JM16003J

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Spotlight

Advertisements